To the modelling of the fatigue cracks propagation in a thin isotropic plates under biaxial asymmetric tension-compression

Plashchynska, Alla

doi:10.17721/1812-5409.2019/1.35

To the modelling of the fatigue cracks propagation in a thin isotropic plates under biaxial asymmetric tension-compression

Тип публікації :

Стаття

Дата випуску :

2019

Автор(и) :

Plashchynska, Alla

Мова основного тексту :

Англійська

eKNUTSHIR URL :

https://ir.library.knu.ua/handle/15071834/26237

DOI :

10.17721/1812-5409.2019/1.35

Журнал :

Bulletin of Taras Shevchenko National University of Kyiv. Physics and Mathematics

Випуск :

1

ISSN :

1812-5409

Початкова сторінка :

154

Кінцева сторінка :

157

Цитування :

[APA 7] Plashchynska, A. (2019). To the modelling of the fatigue cracks propagation in a thin isotropic plates under biaxial asymmetric tension-compression. Bulletin of Taras Shevchenko National University of Kyiv. Physics and Mathematics, (1), 154–157. https://doi.org/10.17721/1812-5409.2019/1.35

[ДСТУ] Plashchynska A. To the modelling of the fatigue cracks propagation in a thin isotropic plates under biaxial asymmetric tension-compression. Bulletin of Taras Shevchenko National University of Kyiv. Physics and Mathematics. 2019. no. 1. P. 154—157. DOI: 10.17721/1812-5409.2019/1.35 (date of access: 18.07.2026).

The modelling of the fatigue fracture process of the thin isotropic infinite plates with cracks under external biaxial asymmetric cyclic loading is considered. The solution of the problem is based on the joint consideration of the fracture mechanics and continuous damage mechanics concepts and using two types of equivalent stress criteria’s. The first one reduces an asymmetrical cyclic load to the equivalent symmetric cyclic load in time of the rupture. The second one reduces a plane stress state in the vicinity of the top crack to a single-axial one. The obtained system of equations of the model a relatively equivalent stress intensity factor allows us to determine the duration of the incubation stage and the rate of fatigue crack propagation in plates with different stress concentrators. The calculated dependences of the crack length, which extends from the circular hole, from the number of load cycles in the infinite aluminum plate with a circular hole at the variation of the parameters of the asymmetrical cycle and the coefficient of the biaxiality loading are constructed.Key words: fatigue crack, biaxial asymmetric cyclic loading, damage.Pages of the article in the issue: 154-157Language of the article: Ukrainian

Файл(и) :

Формат :

Adobe PDF

Розмір :

962.38 KB

Контрольна сума :

(MD5):6c3e848a41296ba3b9789592f4b5e2fd

Якщо не вказано інше, ця робота розповсюджується на умовах ліцензії Creative Commons Attribution 4.0 International