Physicomechanical Properties of Epoxyurethane Biocomposites Strengthened with Hemp Wood Core

Samoilenko, T., Yashchenko, L., Yarova, N., Babich, O., Brovko, O. (2021). Physicomechanical Properties of Epoxyurethane Biocomposites Strengthened with Hemp Wood Core. French-Ukrainian Journal of Chemistry, 9(1), 9–18. https://doi.org/10.17721/fujcV9I1P9-18

Hemp wood core (HWC) filled Si-containing epoxyurethane biocomposites, in which diane epoxy resin was replaced with epoxidized soybean oil (ESO), were obtained. It was shown that the tensile strength of ESO-containing polymer was higher, and the flexural strength was lower than those of original polymer. HWC was especially effective strengthening filler for modified epoxyurethanes, because in that case mechanical properties of composites were higher than those of unfilled polymer matrices. Particularly, flexural and tensile strength of unfilled epoxyurethane with maximum content of ESO were 8.1 and 6.8 MPa respectively, while in corresponding composite they reached 17.3 and 15.7 MPa.