Неділько, С.С.НедількоНаумова, Д.Д.НаумоваВойтенко, Т.Т.Войтенко2026-04-202026-04-202010-09-06Неділько, С., Наумова, Д., Войтенко, Т. (2010). STUDY OF SUBSTITUTING IN Bi - CONTAINING HIGH-TEMPERATURE SUPERCONDUCTING CERAMICS. Вісник Київського національного університету імені Тараса Шевченка. Хімія(1 (48)), 4–5.https://ir.library.knu.ua/handle/15071834/16361Formation of high-temperature superconducting ceramics of composition of Bi2-xLnxSr2CaCu2Oy, was investigated. Effect of Віreplacement for La, Nd, Eu, Ho, Er, Lu on the crystalline structure and critical temperature was shown.Our XRD studies of theBi2-хLnxSr2CaCu2Oу (Ln- La, Nd, Eu, Ho, Er, Lu) system showed that in case of Ln-La with the increase of degree of substituting forx there is an increase of parameters a and c. For Ln- Nd, Eu, Ho, Er, Lu with the increase of degree of substituting x parametersa and c decrease.Temperature of passing into the superconducting state for samples with replacement of Bi3+/ln3+ decrease, incomparison to the clean Bi2212 phase.Досліджено утворення ВТНП сполук складу Bi2-xLnxSr2CaCu2Oy, встановлено вплив заміщення Ві на La, Nd, Eu, Ho, Er, Lu накристалічну будову та температуру переходу у надпровідний стан. Рентгенографічні дослідження показали, що в системіBi2-хLnxSr2CaCu2Oу (Ln- La, Nd, Eu, Ho, Er, Lu) у випадку Ln-La зі збільшенням ступеня заміщення x спостерігається збільшенняпараметрів a та с. Для Ln- Nd, Eu, Ho, Er, Lu зі збільшенням ступеня заміщення х параметри а і с зменшуються. Температура переходу у надпровідний стан для зразків із заміщенням типу Bi3+/Ln3+ знижується, в порівнянні з чистою Bi2212 фазою.uk----Стаття